TECHNOMELT PA 6238 

TECHNOMELT PA 6238

TECHNOMELT PA 6238 Thermoplastic Hot Melt Adhesive

Known as MACROMELT 6238又被称为 MACROMELT 6238

国际胶粘巨头德国汉高TECHNOMELT PA 6238

TECHNOMELT PA 6238 - Polyamide adhesive - Henkel Adhesives

功能与优点 Features and Benefits：

Available in:

20 kg Sack (valve)

TECHNOMELT PA 6238

高可持续性的热熔胶，适合用于金属和塑料，尤其是增塑PVC。具有良好的耐油、耐高温性能。

Hotmelt adhesive, highly sustainable and suited to metals and plastics, particularly plasticized PVC. Good resistance to oils and high temperature.

TECHNOMELT PA 6238是一种琥珀色聚酰胺热熔胶粘剂，由可再生原料制成。它对金属和塑料具有良好的粘合力，特别适用于增塑PVC。具有良好的耐油、耐温性能。它通过热熔胶枪或熔化设备进行半自动或全自动涂施。

TECHNOMELT? PA 6238 is an amber-colored, polyamide hotmelt adhesive formulated from renewable raw materials. It provides good adhesion to metals and plastics and is particularly suited to plasticized PVC. It has good resistance to oils and high temperatures. It is applied via a hotmelt gun or a choice of melting units for semi- or fully automated production.

nourde low pressure molding material solutions.

· 无溶剂

· 基于可再生原料

· 对金属和塑料具有良好的粘合力

· 适用于增塑PVC

· 耐油

· Solvent-free

· Based on renewable raw materials

· Suitable for plasticized PVC

· Good adhesion to metals and plastics

· Oil resistant

Technology Polyamide

Product Type Hotmelt

Cure Physical setting

Condition Thermoplastic

Components One-component

Application General assembly

Color Amber

Density, g/cm3

ISO 1183-1, 20℃

0.98

Softening point, ℃

ASTM E28 (in glycerine)

135 to 145

Melting Viscosity at 160 ℃, mPas 27,000

Elongation, %

ISO 527, Specimen no.5

Cross-head-speed: 50mm/min

500

Low temperature flexibility, ℃

ASTM D 3111

-10

Application:

Application Temperature : 180 to 220 ℃.

Application System : Hotmelt application systems

When bonding to a substrate with high thermal conductivity

the use of a specific application temperature is required for

good wetting.

Storage:

When properly stored in a cool, dry location, with the

container tightly closed when not in use, this product will have

a shelf life of at least 24 months.