Zytel MT409AHS BK010 PA66增韧热稳定

产品描述：

增韧、热稳定、聚酰胺 66

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	348000	160000	psi	ISO 527-1
Tensile Stress (Yield)	8850	6240	psi	ISO 527-2
Tensile Strain (Yield)	5.0	28	%	ISO 527-2
Nominal Tensile Strain at Break	25	> 50	%	ISO 527-2
Flexural Modulus	319000	145000	psi	ISO 178
Flexural Stress	10900	--	psi	ISO 178
Poisson's Ratio	0.38	0.45
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-40°F	5.7	5.7	ft·lb/in2
-22°F	6.2	5.7	ft·lb/in2
73°F	8.1	19	ft·lb/in2
Charpy Unnotched Impact Strength				ISO 179/1eU
-22°F	No Break	No Break
73°F	No Break	No Break
Notched Izod Impact Strength				ISO 180/1A
-40°F	5.2	--	ft·lb/in2
-22°F	6.2	7.1	ft·lb/in2
73°F	8.1	43	ft·lb/in2

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed	369	--	°F	ISO 75-2/B
264 psi, Unannealed	149	--	°F	ISO 75-2/A
Glass Transition Temperature 3	176	68.0	°F	ISO 11357-2
Melting Temperature 3	504	--	°F	ISO 11357-3
CLTE				ISO 11359-2
Flow	5.6E-5	--	in/in/°F
Transverse	5.6E-5	--	in/in/°F
Thermal Conductivity	1.5	--	Btu·in/hr/ft2/°F	ISO 22007-2

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate 4 (0.0394 in)	1.1	--	in/min	ISO 3795
Flame Rating
0.031 in	HB	--		UL 94
0.06 in	HB	--		UL 94, IEC 60695-11-10, -20
0.03 in	HB	--		IEC 60695-11-10, -20
Oxygen Index	21	--	%	ISO 4589-2
FMVSS Flammability	B	--		FMVSS 302

	Dry	Unit
Drying Temperature	176	°F
Drying Time - Desiccant Dryer	2.0 to 4.0	hr
Suggested Max Moisture	< 0.20	%
Processing (Melt) Temp	536 to 572	°F
Melt Temperature, Optimum	554	°F
Mold Temperature	122 to 212	°F
Mold Temperature, Optimum	176	°F
Holding Pressure	7250 to 14500	psi
Drying Recommended	yes
Hold Pressure Time	4.00	s/mm
Maximum Screw Tangential Speed	709	in/min
Extrusion	Dry	Unit
Drying Temperature	< 176	°F
Drying Time	2.0 to 4.0	hr
Suggested Max Moisture	< 0.20	%
Melt Temperature	536 to 572	°F
Extrusion Melt Temperature, Optimum	554	°F