Amodel AS-4133 L PPA玻璃纤维增强

产品描述：

Amodel® AS-4133 L 聚邻苯二甲酰胺 (PPA) 是一种 33% 玻璃纤维增强、润滑、结构等级的聚邻苯二甲酰胺 (PPA)，可提供快速循环时间并且可热水成型。典型应用包括电气和电子元件。

• 黑色：AS-4133 L BK 324

• 自然色：AS-4133 L NT

  Physical	Dry	Conditioned	Unit	Test Method
  Density / Specific Gravity
  --	1.45	--		ASTM D792
  --	1.45	--	g/cm3	ISO 1183/A
  Molding Shrinkage				ASTM D955
  Flow	5.0E-3	--	in/in
  Across Flow	0.010	--	in/in
  Water Absorption 2 (24 hr, 73°F)	0.29	--	%	ASTM D792

  Mechanical	Dry	Conditioned	Unit	Test Method
  Tensile Modulus	1.70E+6	1.70E+6	psi	ASTM D638
  Tensile Strength (Break)	29000	25000	psi	ASTM D638
  Tensile Elongation (Break)	2.5	2.2	%	ASTM D638
  Flexural Modulus	1.60E+6	1.60E+6	psi	ASTM D790
  Flexural Strength (Yield)	42000	35000	psi	ASTM D790
  Compressive Strength	26000	25000	psi	ASTM D695
  Shear Strength	13100	11000	psi	ASTM D732
  Poisson's Ratio	0.41	--		ASTM E132
  Impact	Dry	Conditioned	Unit	Test Method
  Notched Izod Impact	1.5	1.3	ft·lb/in	ASTM D256
  Unnotched Izod Impact	18	--	ft·lb/in	ASTM D4812

  Thermal	Dry	Conditioned	Unit	Test Method
  Deflection Temperature Under Load				ASTM D648
  66 psi, Annealed, 0.125 in	608	--	°F
  264 psi, Annealed, 0.125 in	572	--	°F
  Melting Temperature	608	--	°F	ASTM D3418, DSC
  CLTE				ASTM E831
  Flow : 32 to 194°F	1.2E-5	--	in/in/°F
  Flow : 300 to 480°F	7.8E-6	--	in/in/°F
  Transverse : 32 to 194°F	3.3E-5	--	in/in/°F
  Transverse : 300 to 480°F	6.7E-5	--	in/in/°F

  Electrical	Dry	Conditioned	Unit	Test Method
  Comparative Tracking Index (CTI)	600	600	V	UL 746A
  High Voltage Arc Tracking Rate (HVTR)	0.551	0.709	in/min	UL 746A
  Flammability	Dry	Conditioned	Unit	Test Method
  Flame Rating 3 (0.13 in)	HB	--		UL 94

  Injection	Dry	Unit
  Drying Temperature	248 to 275	°F
  Drying Time	4.0	hr
  Suggested Max Moisture	0.030 to 0.060	%
  Rear Temperature	605 to 615	°F
  Front Temperature	620 to 630	°F
  Processing (Melt) Temp	625 to 650	°F
  Mold Temperature	151 to 284	°F
  Injection Notes