航空航天PPA Amodel AS-9950 HS

产品描述：

Amodel® Supreme AS-9950 HS 是一种 50% 玻璃纤维增强的热稳定聚邻苯二甲酰胺 (PPA)，具有市场上所有 PPA 中 的热机械性能。Amodel® AS 系列专为结构应用和厚壁部件 (>3 mm) 配制，具有比标准 Amodel® PPA 产品更高的熔接线强度。优异的抗蠕变性和低吸湿性也是该树脂的特征。高温下非常高的机械性能、高热变形温度、出色的水解稳定性、耐乙二醇性和耐化学性使该材料成为汽车、航空航天、消费和工业应用中金属替代品的理想选择。

• 黑色：AS-9950 HS BK 324

  Physical	Nominal Value	Unit	Test Method
  Density (73°F)	1.62	g/cm3	ISO 1183/A
  Molding Shrinkage			ASTM D955
  Flow	2.0E-3	in/in
  Across Flow	8.0E-3	in/in
  Water Absorption (24 hr)	0.12	%	ASTM D570

  Mechanical	Nominal Value	Unit	Test Method
  Tensile Modulus
  --	2.57E+6	psi	ASTM D638
  73°F	2.45E+6	psi	ISO 527-1
  212°F	2.34E+6	psi	ISO 527-1
  302°F	1.68E+6	psi	ISO 527-1
  392°F	986000	psi	ISO 527-1
  Tensile Stress
  Break	37600	psi	ASTM D638
  Break, 73°F	33200	psi	ISO 527-2
  Break, 212°F	26100	psi	ISO 527-2
  Break, 302°F	16200	psi	ISO 527-2
  Break, 392°F	8990	psi	ISO 527-2
  Tensile Elongation
  Break	2.4	%	ASTM D638
  Break, 73°F	2.2	%	ISO 527-2
  Break, 212°F	1.9	%	ISO 527-2
  Break, 302°F	2.7	%	ISO 527-2
  Break, 392°F	4.5	%	ASTM D638
  Flexural Modulus
  --	2.42E+6	psi	ASTM D790
  73°F	2.41E+6	psi	ISO 178
  Flexural Strength
  Break	49300	psi	ASTM D790
  Break	49000	psi	ISO 178
  Impact	Nominal Value	Unit	Test Method
  Notched Izod Impact Strength (73°F)	5.1	ft·lb/in2	ISO 180
  Unnotched Izod Impact Strength	32	ft·lb/in2	ISO 180

  Thermal	Nominal Value	Unit	Test Method
  Deflection Temperature Under Load (264 psi, Unannealed)	561	°F	ISO 75-2/A
  Melting Temperature	612	°F	ISO 11357-3
  CLTE			ISO 11359-2
  Flow : -40 to 50°F	7.4E-6	in/in/°F
  Flow : 50 to 140°F	6.4E-6	in/in/°F
  Flow : 140 to 230°F	6.2E-6	in/in/°F
  Flow : 302 to 392°F	4.6E-6	in/in/°F
  Transverse : -40 to 50°F	2.7E-5	in/in/°F
  Transverse : 50 to 140°F	2.7E-5	in/in/°F
  Transverse : 140 to 230°F	2.9E-5	in/in/°F

  Electrical	Nominal Value	Unit	Test Method
  Surface Resistivity	8.1E+16	ohms	ASTM D257
  Volume Resistivity	1.1E+16	ohms·cm	ASTM D257
  Dielectric Strength (0.125 in)	400	V/mil	ASTM D149
  Dielectric Constant (1 MHz)	4.40		ASTM D150
  Dissipation Factor (1 MHz)	0.012		ASTM D150
  Comparative Tracking Index
  --	> 600	V	ASTM D3638
  --	600	V	IEC 60112

  Injection	Nominal Value	Unit
  Drying Temperature	248	°F
  Drying Time	4.0	hr
  Suggested Max Moisture	0.030 to 0.060	%
  Rear Temperature	595 to 626	°F
  Middle Temperature	595 to 626	°F
  Front Temperature	619 to 642	°F
  Processing (Melt) Temp	626 to 662	°F
  Mold Temperature	356	°F